The impact of particle reinforcement with Al2O3, TiB2, and TiC and severe plastic deformation treatment on the combination of strength and electrical conductivity of pure aluminum

doi:10.3390/met9010065

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

Add to "Quick Collection"

Description	Size	Format
The impact of particle reinforcement with Al2O3, TiB2, and TiC and severe plastic deformation treatment on the combination of strength and electrical conductivity of pure aluminum	2 MB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.3390/met9010065

#алюминий

#механические свойства

#электропроводность

#деформационная обработка

#пластическая деформация

Title: The impact of particle reinforcement with Al2O3, TiB2, and TiC and severe plastic deformation treatment on the combination of strength and electrical conductivity of pure aluminum
Creator: Kozulin, Alexander A.
|
Khrustalyov, Anton P.
|
Matveev, Alexey E.
|
Platov, Vladimir V.
|
Vorozhtsov, Alexander B.
|
Zhukova, Tatyana V.
|
Promakhov, Vladimir V.
|
Zhukov, Ilya A.
Date: 2019
DOI: 10.3390/met9010065
Description: It has been found that a high electrical conductivity of 63.1%, the International Annealed Copper Standard (IACS), and high mechanical properties are achieved by the initial aluminum alloy after undergoing four cycles of the severe plastic deformation (SPD) process. It has been found that when TiB2 particles are introduced into aluminum and the samples are subject to SPD, the mechanical characteristics of the aluminum alloy are improved. Microhardness (HV) increases from 329 to 665 MPa, yield strength (YS) increases from 38 to 103 MPa, and ultimate tensile strength (UTS) increases from 73 to 165 MPa while maintaining the initial electrical conductivity of cast aluminum without reinforcing particles (53.9–54.1% IACS).

Relationships: Show Relationship Browser for this Object
collection(s): Физико-технический факультет | Научное управление
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Metals. 2019. Vol. 9, № 1. P. 65 (1-10)
Language: eng