Microstructure and superelastic properties of FeNiCoAlTi single crystals with the <100> orientation under tension

doi:10.3390/cryst12040548

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

Lee, Po-Yu

Add to "Quick Collection"

Description	Size	Format
Microstructure and superelastic properties of FeNiCoAlTi single crystals with the <100> orientation under tension	4 MB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.3390/cryst12040548

#сверхэластичность

#сплавы с памятью формы

#монокристаллы

#сверхупругие свойства

Title: Microstructure and superelastic properties of FeNiCoAlTi single crystals with the <100> orientation under tension
Creator: Tseng, Li-Wei
|
Chen, Chih-Hsuan
|
Tzeng, Yu-Chih
|
Lee, Po-Yu
|
Lu, Nian-Hu
|
Chumlyakov, Yuri I.
Date: 2022
DOI: 10.3390/cryst12040548
Description: The microstructure and superelastic response of an Fe41 Ni28 Co17 Al11.5 Ti2.5 (at.%) single crystal along the [removed] orientation was investigated under tension at room temperature after aging at 600◦ C for 24 h. From the superelastic results, the samples aged at 600◦ C for 24 h exhibited 4.5% recoverable strain at room temperature. The digital image correlation (DIC) method was used to observe the strain distribution during the 6.5% applied strain loading. The DIC results showed that the strain was uniformly distributed during the loading and unloading cycles. Only one martensite variant was observed from the DIC results. This was related to the aging heat treatment times. The martensite morphology became a single variant with a longer aging time. The thermo-magnetization results indicated that the phase transformation and temperature hysteresis was around 36◦ C. Increasing the magnetic field from 0.05 to 7 Tesla, the transformation temperatures increased. The maximum magnetization was 160 emu/g under the magnetic field of 7 Tesla. From the transmission electron microscopy results, the L12 precipitates were around 10 nm in size, and they were high in Ni content and low in Fe content.

Relationships: Show Relationship Browser for this Object
collection(s): Сибирский физико-технический институт
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Crystals. 2022. Vol. 12, № 4. P. 548 (1-8)
Language: eng

Created: 21-02-2023

967 Visitors

882 Hits

107 Downloads

Сибирский физико-технический институт Microstructure and superelastic properties of FeNiCoAlTi single crystals with the <100> orientation under tension