Structural-phase state of UFG-titanium implanted with aluminum ions

doi:10.4028/www.scientific.net/SSP.303.161

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

Add to "Quick Collection"

Description	Size	Format
Structural-phase state of UFG-titanium implanted with aluminum ions	785 KB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.4028/www.scientific.net/SSP.303.161

#титан

#растровая электронная микроскопия

#структурно-фазовое состояние

Title: Structural-phase state of UFG-titanium implanted with aluminum ions
Creator: Nikonenko, Alisa V.
|
Popova, N. A.
|
Nikonenko, Elena L.
|
Kalashnikov, Mark P.
|
Kurzina, Irina A.
Date: 2020
DOI: 10.4028/www.scientific.net/SSP.303.161
Description: Transmission electron microscopy investigations were carried out to study the structuralphase state of ultra-fine grain (UFG) titanium with the average grain size of ~0.2 µm, implanted with aluminum ions. Implantation was carried out on MEVVA-V.RU ion source at room temperature, exposure time of 5.25 h and ion implantation dosage of 1⋅1018 ion/cm2. UFG-titanium was obtained by a combined multiple uniaxial compaction with rolling in grooved rolls and further annealing at 573 К for 1h. The specimens were investigated before and after implantation at a distance of 70-100 nm from the specimen surface. Concentration profile of aluminum implanted with α-Ti was obtained. It was revealed that the thickness of implanted layer was 200 nm, while maximum aluminum concentration was 70 at.%. Implantation of aluminum into titanium has resulted in formation of the whole number of phases having various crystal lattices, like β-Ti, TiAl3, Ti3Al, TiC and TiO2. The areas of their localization, the sizes, distribution density and volume fractions were determined. Grain distribution functions by their sizes were built, and the average grain size was defined. The paper investigates the influence of implantation on the grain anisotropy factor. It was revealed that implantation leads to the decrease in the average transverse and longitudinal grain size of α-Ti and decrease in the anisotropy factor by three times. The yield stress and contributions of separate strengthening mechanisms before and after implantation were calculated. The implantation has resulted in increase in the yield stress by two times.

Relationships: Show Relationship Browser for this Object
collection(s): Химический факультет
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Solid state phenomena. 2020. Vol. 303. P. 161-168