In this paper porous ceramics based on the Zr02-Mg0 system were studied. It was shown, that the addition of an organic pore-forming particles make it possible to obtain a bimodal pore structure. X-ray diffraction analysis showed that with the increasing of MgO concentration, the average size of Zr02 and MgO crystallites grows up and their crystal lattice microdistortion decrease. Strength with increasing of MgO concentration is increasing and the dependence of compressive strength from microstresses was found.
Перспективы развития фундаментальных наук : сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, 24-27 апреля 2018 г.. Томск, 2018. Т. 1 : Физика. С. 78-80
Language
rus
1186 Visitors1036 Hits167 Downloads
Физико-технический факультет
Влияние микроструктуры и фазового состава на механические свойства композита ZrO2-MgO с бимодальной поровой структурой