Acoustic emission and DSC investigations of anomalous stress-stain curves and burst like shape recovery of Ni49Fe18Ga27Co6 shape memory single crystals

doi:10.1016/j.intermet.2023.107932

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

сплавы с памятью формы | эффект памяти формы

Add to "Quick Collection"

Description	Size	Format
Acoustic emission and DSC investigations of anomalous stress-stain curves and burst like shape recovery of Ni49Fe18Ga27Co6 shape memory single crystals	698 KB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.1016/j.intermet.2023.107932

#сплавы с памятью формы

#мартенситное превращение

#эффект памяти формы

#дифференциальная сканирующая калориметрия

#акустико-эмиссионная спектроскопия

Title: Acoustic emission and DSC investigations of anomalous stress-stain curves and burst like shape recovery of Ni49Fe18Ga27Co6 shape memory single crystals
Creator: Kamel, Sarah M.
|
Daróczi, Lajos
|
Tóth, László Z.
|
Panchenko, Elena Yu.
|
Chumlyakov, Yuri I.
|
Samy, Nora M.
|
Beke, Dezső L.
Date: 2023
DOI: 10.1016/j.intermet.2023.107932
Description: Simultaneous acoustic emission, AE, and DSC measurements under compression along [110]A direction were carried out on Ni49Fe18Ga27Co6 shape memory single crystals. The compression resulted in anomalous stressstrain loops with stress drops/jumps on it, reflecting a sudden formation/dissolution of a more stable (detwinned) martensite structural modification than the thermally induced (twinned) one. The final detwinned martensite, obtained below a certain temperature, was stable even after downloading: during heating it showed a burst-like recovery at about 35K higher transformation temperature than that of the thermally induced one, with an audible click. It was obtained that the number of acoustic events showed strong asymmetry: e.g. for stress induced transformations the number of hits for uploading was larger. Simultaneous measurements of stress-time curves and AE versus time revealed that in the nucleation/dissolution processes in both (up and down) directions, as an intermediate step, the twinned martensite was first formed and resulted in additional AE events. This was interpreted by the easy as well as difficult nucleation of the twinned and detwinned martensites, respectively. The stress drops on the uploading stress-strain curve were attributed to subsequent nucleation of the detwinned martensite from the twinned modification and were followed by a sharp decrease of the AE activity. This indicated that the formation of detwinned martensite is a sudden, fast process and can take place without significant elastic energy storage. This was also in agreement with the fact that during burst like thermal recovery the width of the transition was very small (Af ≅ As). Similarly, during downloading the stress jumps were interpreted as sudden dissolutions of the detwinned phase by retwinning and at all stress jumps there were local maxima on the AE activity curve.

Relationships: Show Relationship Browser for this Object
collection(s): Сибирский физико-технический институт
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Intermetallics. 2023. Vol. 159. P. 107932 (1-13)
Language: eng

Created: 14-02-2024

1357 Visitors

1242 Hits

161 Downloads

Сибирский физико-технический институт Acoustic emission and DSC investigations of anomalous stress-stain curves and burst like shape recovery of Ni49Fe18Ga27Co6 shape memory single crystals