Electrospun magnetic composite poly-3-hydroxybutyrate/magnetite scaffolds for biomedical applications: composition, structure, magnetic properties, and biological performance

doi:10.1021/acsabm.2c00496

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

Add to "Quick Collection"

Description	Size	Format
Electrospun magnetic composite poly-3-hydroxybutyrate/magnetite scaffolds for biomedical applications: composition, structure, magnetic properties, and biological performance	25 MB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.1021/acsabm.2c00496

#композитные каркасы

#поли-3-гидроксибутират

#электропрядение

#намагничивание

#магнитные свойства

#биологические характеристики

Title: Electrospun magnetic composite poly-3-hydroxybutyrate/magnetite scaffolds for biomedical applications: composition, structure, magnetic properties, and biological performance
Creator: Pryadko, Artyom S.
|
Mukhortova, Yulia R.
|
Chernozem, Roman V.
|
Pariy, Igor O.
|
Alipkina, Svetlana I.
|
Zharkova, Irina I.
|
Dudun, Andrey A.
|
Zhuikov, Vsevolod A.
|
Moisenovich, Anastasia M.
|
Bonartseva, Garina A.
|
Voinova, Vera V.
|
Chesnokova, Dariana V.
|
Ivanov, Alexey A.
|
Travnikova, Daria Yu.
|
Shaitan, Konstantin V.
|
Bonartsev, Anton P.
|
Wagner, Dmitriy V.
|
Shlapakova, Lada E.
|
Surmenev, Roman A.
|
Surmeneva, Maria A.
Date: 2022
DOI: 10.1021/acsabm.2c00496
Description: Magnetically responsive composite polymer scaffolds have good potential for a variety of biomedical applications. In this work, electrospun composite scaffolds made of polyhydroxybutyrate (PHB) and magnetite (Fe3O4) particles (MPs) were studied before and after degradation in either PBS or a lipase solution. MPs of different sizes with high saturation magnetization were synthesized by the coprecipitation method followed by coating with citric acid (CA). Nanosized MPs were prone to magnetite-maghemite phase transformation during scaffold fabrication, as revealed by Raman spectroscopy; however, for CA-functionalized nanoparticles, the main phase was found to be magnetite, with some traces of maghemite. Submicron MPs were resistant to the magnetite-maghemite phase transformation. MPs did not significantly affect the morphology and diameter of PHB fibers. The scaffolds containing CA-coated MPs lost 0.3 or 0.2% of mass in the lipase solution and PBS, respectively, whereas scaffolds doped with unmodified MPs showed no mass changes after 1 month of incubation in either medium. In all electrospun scaffolds, no alterations of the fiber morphology were observed. Possible mechanisms of the crystalline-lamellar-structure changes in hybrid PHB/Fe3O4 scaffolds during hydrolytic and enzymatic degradation are proposed. It was revealed that particle size and particle surface functionalization affect the mechanical properties of the hybrid scaffolds. The addition of unmodified MPs increased scaffolds' ultimate strength but reduced elongation at break after the biodegradation, whereas simultaneous increases in both parameters were observed for composite scaffolds doped with CA-coated MPs. The highest saturation magnetization-higher than that published in the literature-was registered for composite PHB scaffolds doped with submicron MPs. All PHB scaffolds proved to be biocompatible, and the ones doped with nanosized MPs yielded faster proliferation of rat mesenchymal stem cells. In addition, all electrospun scaffolds were able to support angiogenesis in vivo at 30 days after implantation in Wistar rats.

Relationships: Show Relationship Browser for this Object
collection(s): Радиофизический факультет
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: ACS applied bio materials. 2022. Vol. 5, № 8. P. 3999-4019
Language: eng

Created: 11-04-2023

3207 Visitors

2945 Hits

355 Downloads

Радиофизический факультет Electrospun magnetic composite poly-3-hydroxybutyrate/magnetite scaffolds for biomedical applications: composition, structure, magnetic properties, and biological performance