Shape memory effect and superelasticity of [001]-oriented FeNiCoAlNb single crystals aged under and without stress

doi:10.3390/met11060943

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

Add to "Quick Collection"

Description	Size	Format
Shape memory effect and superelasticity of [001]-oriented FeNiCoAlNb single crystals aged under and without stress	3 MB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.3390/met11060943

#сплавы на основе железа

#монокристаллы

#сверхэластичность

#эффект памяти формы

Title: Shape memory effect and superelasticity of [001]-oriented FeNiCoAlNb single crystals aged under and without stress
Creator: Chumlyakov, Yuri I.
|
Kireeva, Irina V. (физик)
|
Pobedennaya, Zinaida V.
|
Krooß, Philipp
|
Niendorf, Thomas
Date: 2021
DOI: 10.3390/met11060943
Description: The two-step ageing of Fe-28Ni-17Co-11.5Al-2.5Nb (at.%) single crystals under and without stress, leads to the precipitation of the γ'- and β-phase particles. Research has shown that γ–α' thermoelastic martensitic transformation (MT), with shape memory effect (SME) and superelasticity (SE), develops in the [001]-oriented crystals under tension. SE was observed within the range from the temperature of the start of MT upon cooling Ms, to the temperature of the end of the reverse MT upon heating Af, and at temperatures from Af to 323–373 K. It was found that at γ–α' MT in the [001]- oriented crystals, with γ' - and β-phase particles, a high level of elastic energy, ∆Gel, is generated, which significantly exceeds the energy dissipation, ∆Gdis. As a result, the temperature of the start of the reverse MT, while heating As, became lower than the temperature Ms. The development of γ–α' MT under stress occurs with high values of the transformation hardening coefficient, Θ = dσ/dε from 2 to 8 GPa and low values of mechanical ∆σ and thermal ∆Th hysteresis. The reasons for an increase in ∆Gel during the development of γ–α' 0 MT under stress are discussed.

Relationships: Show Relationship Browser for this Object
collection(s): Сибирский физико-технический институт
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Metals. 2021. Vol. 11, № 6. P. 943 (1-15)
Language: eng

Created: 08-11-2022

827 Visitors

729 Hits

106 Downloads

Сибирский физико-технический институт Shape memory effect and superelasticity of [001]-oriented FeNiCoAlNb single crystals aged under and without stress