Effect of multistage high temperature thermomechanical treatment on the microstructure and mechanical properties of austenitic reactor steel

doi:10.3390/met12010063

Эндаумент фонд ТГУ!
Впиши своё имя в историю университета
- Сделать пожертвование -

2022 | механические свойства

Add to "Quick Collection"

Description	Size	Format
Effect of multistage high temperature thermomechanical treatment on the microstructure and mechanical properties of austenitic reactor steel	7 MB	Adobe Acrobat PDF	Read	Download
DOI Доступ к ресурсу на сайте издателя			10.3390/met12010063

#реакторная сталь

#аустенитная сталь

#высокотемпературная термомеханическая обработка

#электронная микроскопия

#деформации микроструктуры

#измельчение зерна

#двойникование

#механические свойства

#зубчатый поток

Title: Effect of multistage high temperature thermomechanical treatment on the microstructure and mechanical properties of austenitic reactor steel
Creator: Akkuzin, Sergey A.
|
Litovchenko, Igor Yu.
|
Polekhina, Nadezhda A.
|
Almaeva, Kseniya V.
|
Kim, Anna
|
Moskvichev, Evgeny N.
|
Chernov, Vyacheslav M.
Date: 2022
DOI: 10.3390/met12010063
Description: The deformation microstructures formed by novel multistage high-temperature thermomechanical treatment (HTMT) and their effect on the mechanical properties of austenitic reactor steel are investigated. It is shown that HTMT with plastic deformation at the temperature decreasing in each stage (1100, 900, and 600 C with a total strain degree of e = 2) is an effective method for refining the grain structure and increasing the strength of the reactor steel. The structural features of grains, grain boundaries and defective substructure of the steel are studied in two sections (in planes perpendicular to the transverse direction and perpendicular to the normal direction) by Scanning Electron Microscopy with Electron Back-Scatter Diffraction (SEM EBSD) and Transmission Electron Microscopy (TEM). After the multistage HTMT, a fragmented structure is formed with grains elongated along the rolling direction and flattened in the rolling plane. The average grain size decreases from 19.3 m (for the state after solution treatment) to 1.8 m. A high density of low-angle boundaries (up to 80%) is found inside deformed grains. An additional cold deformation (e = 0.3) after the multistage HTMT promotes mechanical twinning within fragmented grains and subgrains. The resulting structural states provide high strength properties of steel: the yield strength increases up to 910 MPa (at 20 C) and up to 580 MPa (at 650 C), which is 4.6 and 6.1 times higher than that in the state after solution treatment (ST), respectively. The formation of deformed substructure and the influence of dynamic strain aging at an elevated tensile temperature on the mechanical properties of the steel are discussed. Based on the results obtained, the multistage HTMT used in this study can be applied for increasing the strength of austenitic steels.

Relationships: Show Relationship Browser for this Object
collection(s): Научное управление | Физический факультет
Identifier: смотреть в электронном каталоге НБ ТГУ
Type: статьи в журналах
Source: Metals. 2022. Vol. 12, № 1. P. 63 (1-16)
Language: eng

Created: 02-09-2022

3413 Visitors

3274 Hits

170 Downloads

Научное управление

Физический факультет Effect of multistage high temperature thermomechanical treatment on the microstructure and mechanical properties of austenitic reactor steel