In work, AlMgBi4-TiB2 composite materials were obtained by SHS and subsequent spark plasma sintering. Phase composition of obtained composite material was represented by AlMgBj4, MgAl2O4, TiB2 and AlB12 phases. The hardness of produced sample is 32 GPa.